Suitable for use as a dual coat system for protecting and embellishing metal objects that are regularly exposed to high temperatures (300 to 600°C) such as fitted hearths, stoves, barbecue stands, car exhausts, sauna’s, etc.
| Colour | 3535 Red |
| Appearance when dry | Mat |
| Packaging | 5KG / 20 KG |
| Max operating temperature | 300°C – 600°C |
| Solid matter content (by weight) depending on formulation | 50% |
| Surface preparation | Remove grease, oil and all other surface contaminations The surface must be clean and dry during application. Surface blasting in accordance with SA 2 ½ is advised Nonetheless, good results can be obtained with thorough cleaning and mechanical removal of all traces of rust |
| Application | Apply using a low pressure conventional spray gun (with or without electrostatic spraying equipment) Thorough mechanical stirring is recommended in order to obtain a homogenous product |
| Application conditions | +5°C and surface temperature at 3°C above dew point |
| Theoretical coverage | 15.5 m²/L for dry film thickness of 20 μm |
| Recommended film thickness | 20 (± 5) μm |
| Recommended drying conditions | Air drying system. Optimum properties (fully cured, chemical resistance to oil, diesel and gasoline) apply after heating above 220°C for 1 hour. Dust dry after 15 minutes at 20°C |
| Recoatable | 1-2 hours at room temperature |
| Shelf Life / Storage Conditions ( +5C°< T <35°) |
6 months in original unopened packaging, protected from moisture, extreme cold and excessive heat |
Established in 1969 PLPCOATINGS has continually extended its knowledge in a diverse range of surface treatments.
All products are a result of extensive research and development and currently used by Europe’s leading manufacturers.